Description

 W-20 seriers 

   Webster Aluminum alloy metal hardness tester

 

Introduction  

 

 Present,our company have 3 type of Webster hardness,w-20,w-20a,w-20b.W-20 type refer to USA ANSI/ASTM B647-87 standard.Also comply with China Nonferrous Metal Industry YS/T420-2000 ” aluminum Webster hardness test method” a universal standard aluminum instrumentation.W-20a type in Merriam Webster hardness tester is the basis of universal hardness on the production of a measurable 1-13mm thick long, wide , thick industrial profiles of special detection equipment . W-20b -based Webster Hardness is based on the same type of Webster Hardness pass on production of a seat attached to a diameter of 5.8mm, 6mm inside diameter between measurable or more small diameter aluminum profiles more than 6mm gap small size profiles and profiles, such as general-purpose radiator Webster Hardness measurements inconvenience aluminum special detection equipment .

 

  W-20 Series Webster Hardness Tester for testing aluminum extrusions , pipes and plates, particularly suitable for the production site , sales site , or a construction site on the hardness of the product for rapid , non-destructive testing. The products are easy to carry , reading intuitive features .

 

 

 

Technical parameter

 

Mainly test Aluminum(1100~7075 series)hardness

 

Test range 0~20HW(Aluminum and aluminum alloy 25~110HRE)

 

                  (copper alloy 60~90HRF)

Accurate measure range 4~17Hw(Determined by the instrument design principles)

 

Accuracy ±0.5HW

 

Resolution 1HW

 

Measuring the thickness w-20 type 1~6mm(Stickers seat diameter 9.5mm)

 

                           W-20a type 1~13mm(Stickers seat diameter 9.5mm)

 

                                        (Post 23.5mm diameter seat coat)

 

                           W-20b type 1~6mm(Block posted straight 5.8mm)